The problem of childbirth is related to the people's livelihood. Whether a country can prosper or not depends on the population. I saw a set of data a few days ago. The data shows that on January 1, 1990, 2,784 babies were born in Shanghai. Ten years later, on January 1, 2000, 1,148 babies were born in Shanghai. In 2010, the number became 380. , 2020 only 156 people, the decline in the birth rate is shocking. The three most critical reasons are: I don't want to give birth, I can't afford it, I can't give birth! The decline of the global population will bring a series of economic and social problems, among which the demand for concrete foaming agent will also be affected.

Concrete is classified as high-strength concrete based on 28-day strength. Until the 1970s, concrete with a strength of more than 40Mpa was classified as high-strength concrete.  The benchmark for high-strength concrete is raised to 55Mpa or higher when concrete mixtures of approximately 60Mpa and above are produced commercially. 

 

High strength concrete has a history of about 35 years, from the development of superplasticizer admixtures in the late 1960s, Japan using "naphthalene sulfonate" high strength prefabricated products, and Germany using "sodium benzenesulfonate" underwater concrete, which was a pioneer in this technology. 

 

How is the high strength of concrete achieved? 

Higher concrete strength can be achieved by using one or a combination of some or many of the following methods: 

High cement content 

Reduce water-cement ratio 

Better machinability and therefore better compaction 

 

Requirements for high-strength concrete require a high content of cementitious material in the concrete mixture, which can be in the range of more than 400 kilograms per cubic meter. Higher cementitious content leads to higher thermal shrinkage and dry shrinkage, and there is a stage where further cementitious material addition does not affect strength.  As for durability, the minimum and maximum cement content in concrete is regulated by law, and reducing the water-cement ratio has its limitations, especially under field conditions. The desire for higher strength leads other materials to achieve the desired effect, thus showing the contribution of cementitious materials to concrete strength. 

 

The addition of pozzolanic mixtures such as pozzolanic fly ash (PFA) or granular blast furnace slag (GGBS) contributes to the formation of secondary CSH gel thereby increasing strength.

 

The addition of pozzolans admixtures (such as fly ash used as an admixture) reduces the strength gain of concrete for the first 3 to 7 days and displays the gain after 7 days and provides higher strength over the long term. 

Add mineral mixtures such as silica fume or metakaolin or rice husk ash. 

 

Silica fume or highly reactive volcanic ash mixtures such as metakaolin and rice husk ash (RHS) will begin to function in about 3 days.  RHS has an advantage over PFA because RHS is more reactive. 

Using chemical admixtures such as superplasticizers or superplasticizers, controlling admixtures will help achieve higher strength in concrete. 

 

Research and experience have shown that admixtures based on polycarboxylic ether (PCE), known as high plasticizers, are best suited for this job as they have a water reduction capacity of 18 to 40 percent relative to control or reference concrete. 

A combination of all or more of the above to achieve the desired strength.


With HSC accompanied by some complexity, such as higher shrinkage rates, higher hydration heat, etc., combinations of at least some of these methods are now unchanged, all of which need to be neutralized or controlled.  Most problems are handled by PFA or a combination of GGBS and PCE mixtures.


Steam curing is also used to speed up cement hydration, but this may not result in higher strength.  Substituting some fine aggregate with fly ash or blast furnace slag can achieve early strength gains without increasing the water requirement of the concrete mixture. 

 

Suppliers of Concrete Additives

TRUNNANO is a reliable foaming agents supplier with over 12-year experience in nano-building energy conservation and nanotechnology development.

If you are looking for high-quality CLC foaming agents, please feel free to contact us and send an inquiry. (sales@cabr-concrete.com)

We accept payment via Credit Card, T/T, West Union, and Paypal. TRUNNANO will ship the goods to customers overseas through FedEx, DHL, by air, or by sea.


A preparation developed in China; the comfort and the multifunctional properties of nanomaterials make "dead skin" capable of sensing again. Electronic skin is artificial skin that mimics the function of human skin. Recently, the world-renowned journal Advanced Science reported a simple and highly programmable electronic skin on a leather substrate developed by a Chinese team, which combines the natural complex structure of leather, the comfort of wearing, and the multi-functional properties of nanomaterials. , so that the "dead skin" has the ability to sense again.

In the future, concrete foaming agent will be used in various high-tech fields, and the market demand for concrete foaming agent will also be great. Please contact us for more information on concrete foaming agent.


Inquiry us

Our Latest Products

Structure of Molybdenum Carbide Mo2C

Molybdenum Carbide, with the chemical formula Mo2C. It has the characteristics of high melting point and hardness, good thermal stability and mechanical stability.…

How is lithium 12-hydroxystearate produced?

Lithium 12-hydroxystearate is widely used in lubricants, stabilizers, bleaching agents, thickeners. Product Name:Lithium 12-Hydroxystearate…

Product Properties of Chromium Oxide Cr2O3 Powder CAS 1308-38-9

Green chrome oxide (Cr2O3 powder) is extremely stable and have excellent weather resistance. It's insoluble in water, acid and organic solvents, slightly soluble in sodium hydroxide solution, only soluble in hot sodium bromate solution, hot concentra…